The basic specification for hot dip galvanized coatings on iron and steel articles is defined by a single standard, EN ISO 1461 ‘Hot dip galvanized coatings on iron and steel articles – specifications and test methods’.
ISO 1461:2009 specifies the general properties of coatings and test methods for coatings applied by dipping fabricated iron and steel articles (including certain castings) in a zinc melt (containing not more than 2% of other metals). It does not apply to the following:. sheet, wire and woven or welded mesh products that are continuously hot dip galvanized;.
tube and pipe that are hot dip galvanized in automatic plants;. hot dip galvanized products (e.g. Fasteners) for which specific standards exist and which might include additional requirements or requirements which are different from those of ISO 1461:2009. After-treatment/over-coating of hot dip galvanized articles is not covered by ISO 1461:2009.
International Standards Organization ISO 1461, Hot Dip Galvanized Coatings on Fabricated Iron and Steel Articles Specifications and Test Methods, is a general galvanizing specification. This specification is essentially equivalent to the American Society of Testing and Materials. (ASTM) A123 and A153. The ISO specification is 15 pages in length and includes 5 appendices.
The appendices include information such as required information to be supplied by the purchaser to the galvanizer, safety and process requirements, coating properties, determination of coating thickness, and a bibliography of other referenced specifications. In comparing the two standards, and and, there are no major differences.
![Din en iso 1461 Din en iso 1461](/uploads/1/2/5/5/125504908/634488705.jpg)
However, small differences do occur. The easiest way to sum up the differences between the two specifications is by comparing the coating thickness requirements in a table. The differences in minimum average coating thickness for most steel articles are small. In the specification, the ISO minimum coating thickness requirements are summed up into one table, which does not mention coating grades and does not require the user to reference two tables as with ASTM A123. Also, the ISO1461 specification lists minimum local coating thickness to which any one measurement must meet. These are 0.4-0.6 mils thinner than the minimum average coating thickness.
In the ASTM specifications, only ASTM A153 has such minimum local thickness coating listed for castings and fasteners. Rolled, pressed and forged articles referred to ASTM A153 also have minimum local coating thickness; these articles are not specifically mentioned in the ISO specification.
After comparing the two, I found that they are very similar, with the ASTM Specs typically requiring more coating thickness on most types and thickens of steel. Therefore, if you can meet ASTM coating requirements, you most likely will meet the ISO 1461 specification, as well.
© 2019 American Galvanizers Association. The material provided herein has been developed to provide accurate and authoritative information about after-fabrication hot-dip galvanized steel. This material provides general information only and is not intended as a substitute for competent professional examination and verification as to suitability and applicability.
The information provided herein is not intended as a representation or warranty on the part of the AGA. Anyone making use of this information assumes all liability arising from such use.